Zirconia Corundum Brick

Description

Zirconia Corundum Brick Introduction
 
RONGSHENG zircon corundum brick is made of a-Al2O3, ZrO2 and zirconium corundum clinker as materials , it is produced by mixing, molding, drying and sintering at high temperature in shuttle kiln.
 
Zircon corundum brick are the most widely used materials both in glass contact and superstructure of glass melting furnaces.The products have passed the ISO international certified, are made of high pure material, fired at high temperature by advanced technology, with the advantages of high strength, high compression resistance, good thermal shock resistance, good performance in high temperature, good thermal conductivity, good erosion resistance and so on. Widely be used for linings of furnace in industries.
 
Zirconia Corundum Brick Product Parameters
 

The parameter of Zirconia corundum brick
Item	AZS-33	AZS-36	AZS-41
Al2O3%	standard	standard	standard
ZrO2%	≥33	≥36	≥41
SiO2%	≤16	≤14	≤13
Fe2O3+TiO2%	≤0.3	≤0.3	≤0.3
Bulk density,g/cm3	3.5-3.6	3.75	3.9
Cold Crushing strength MPa	350	350	350
Thermal expansioncoefficient(1000℃)	0.80	0.80	0.80
Exudation temperature of glass         phase°C	1400	1400	1400
Baddeleyite	32	35	40
Glass phase	21	18	17
α-corundum	47	47	43

 
Zirconia Corundum Bricks Features

1. Raw material is corundum and baddeleyite eutecticum, high compression strength

2.Top high-temperature capablility.

3.Excellent thermal stability.

4.Low thermal conductivity

5.Powerful penetrating-proof capability.

6.Good erosion-resistance.

7.Strong resistant erosion stability to the glass liquid.
 
Zirconia Corundum Brick Manufacturing Process

Made of the zirconite (Industry zirconia ) and industry alumina as the mainly mixed raw material, melting in the electric furnace, casting, annealing, machining, then finished.